Abstract

In order to investigate the thermal fatigue characteristic and high temperature deformation behavior of Cu-W artificial lamellar composite, three patterns of thermal cycles which have different ranges of temperature and holding time at maximum temperature were used and the compression tests were carried out at 773K～973K under strain-rates from 5×10-6s-l to 2×10-4s-1.

アントン·ファン·レーウェンフックはsienceへの貢献に何をしなかった

Plastic deformation of Cu layer of the composite and the interfacial sliding between Cu and W layers were observed during the thermal cycles. The result of the compression test suggests that the mechanical property of the composite depends on the atomic structure of the interface between the layers.

These are our most popular posts:

Residual Stresses and Fatigue Strength in Ceramic/Metal Joints

高温強度. 高温クリープ; 高温疲労; 各種寿命推定法. Ehime University. 高温強度. 高温クリープ. 高温疲労. 各種寿命推定法 ... 高温疲労強度; 高温疲労の特徴; 熱疲労. 線型損傷則; ひずみ範囲分割法. Ehime University. 高温クリープ 一．高温クリープの ... read more

高温低サイクル疲労の英語・英訳 - 英和辞典・和英辞典 Weblio辞書

高温低サイクル疲労を英語に訳すと high temperature low cycle fatigue - 約880万語 ある英和辞典・和英辞典。発音・イディオムも分かる英語辞書。 read more

高温疲労の英語・英訳 - 英和辞典・和英辞典 Weblio辞書

高温疲労を英語に訳すと fatigue at elevated temperature - 約878万語ある英和辞典・ 和英辞典。発音・イディオムも分かる英語辞書。 read more

Word : 高温疲労

高温環境下における疲労現象で，一般に温度が高くなるほど疲労強度が低下する． しかし，炭素鋼などでは青熱脆性の起こる温度域で，Ni基超合金では700～800℃付近 で極大を示すことがある．また，高温疲労強度は負荷の繰返し速度，負荷波形，使用 環境 ... read more